【WANHUA】CLARNATE® FR2720T

WeChat

copy Link

Facebook

Tumblr

General Information
Features •Flammability •Medium-High Viscosity •Easy Release
Uses •Fire resistance
Appearance •Clear/Transparent
Forms •Pellets
Processing Method •Extrusion •Injection Molding

Minimum Order Quantity 25kg

Packaging Details 25kg/bag

Delivery Time 3-5 working days to departure port

Supply Ability 1000MT/Month

Price $1.5-$3

Consult Now

Detail

CLARNATE®FR2720T
		Technical Data Sheet
Revision Date： 2021-03-01			NO .WHPCBU_0001
Name :	FR2720T		Version：3.0
CLARNATE®FR2720T Polycarbonate Resin
		General Information
Features		·Flammability	·Medium-High Viscosity	·Easy Release
Uses		·Fire resistance
Appearance		·Clear/Transparent
Forms		·Pellets
Processing Method		·Extrusion	·Injection Molding
		Typical Properties
		Test Method	Test Condition	Unit	Typical Value
Physical
Melt Flow Index		ASTM D1238	300℃/1.2Kg	g/10min	8
Mold Shrinkage		ASTM D955	-	%	0.5-0.7
WaterAbsorption		ASTM D570	23℃,24h	%	0.2
Density		ASTM D792	-	g/cm³	1.2
Mechanical
Stress at Break		ASTM D638	50mm/min	MPa	70
Tensile Modulus		ASTM D638	1mm/min	MPa	2200
Yield Stress		ASTM D638	50mm/min	MPa	65
Strain at Break		ASTM D638	50mm/min	%	130
Flexural Strength		ASTM D790	2mm/min	MPa	95
Flexural Modulus		ASTM D790	2mm/min	MPa	2300
Izod Notched Impact Strength		ASTM D256	23℃	J/m	900
Thermal
Heat Distortion Temp.		ASTM D648	1.82MPa;3.2mm	℃	129
Vicat Softening Temp.		ASTM D1525	120℃/h;50N	℃	150
Date of issue: Mar. 01, 2021			CLARNATE®
Version： 3.0
			1 / 3

CLARNATE®FR2720T
	Typical Properties
	Test Method	Test Condition	Unit	Typical Value
Optical
Haze	ASTM D1003	3mm	%	0.2
Light Transmittance	ASTM D1003	3mm	%	90
Flammability
	UL 94	1.5mm	-	V0
Processing Condition
Drying Temperature			℃	120
Drying Time			h	5
Injection Temperature			℃	280-300
Mold temperature			℃	80