【WANHUA】CLARNATE® A1225BK

WeChat

copy Link

Facebook

Tumblr

General Information
Features •Low Viscosity •Easy Release •High Gloss
Forms •Black Pellets
Processing Method •Injection Molding

Minimum Order Quantity 25kg

Packaging Details 25kg/bag

Delivery Time 3-5 working days to departure port

Supply Ability 1000MT/Month

Price $1.5-$3

Consult Now

Detail

CLARNATE®A1225BK
		Technical Data Sheet
Revision Date： 2021-03-01				NO .WHPCBU_0001
Name :	A1225BK			Version：3.0
CLARNATE®A1225BK Polycarbonate Resin
		General Information
Features		·Low Viscosity	·Easy Release	·High Gloss
Forms		·Black Pellets
Processing Method		·Injection Molding
		Typical Properties
		Test Method	Test Condition	Unit	Typical Value
Physical
Melt Flow Index		ASTM D1238	300℃/1.2Kg	g/10min	20
Mold Shrinkage		ASTM D955	-	%	0.5-0.7
WaterAbsorption		ASTM D570	23℃,24h	%	0.2
Density		ASTM D792	-	g/cm³	1.2
Mechanical
Stress at Break		ASTM D638	50mm/min	MPa	65
Tensile Modulus		ASTM D638	1mm/min	MPa	2300
Yield Stress		ASTM D638	50mm/min	MPa	65
Strain at Break		ASTM D638	50mm/min	%	130
Flexural Strength		ASTM D790	2mm/min	MPa	90
Flexural Modulus		ASTM D790	2mm/min	MPa	2350
Izod Notched Impact Strength		ASTM D256	23℃	J/m	650
Thermal
Heat Distortion Temp.		ASTM D648	1.82MPa;3.2mm	℃	127
Vicat Softening Temp.		ASTM D1525	120℃/h;50N	℃	147
Date of issue: Mar. 01, 2021				CLARNATE®
Version： 3.0
			1 / 3

CLARNATE®A1225BK
	Typical Properties
	Test Method	Test Condition	Unit	Typical Value
Optical
Haze	ASTM D1003	3mm	%	--
Light Transmittance	ASTM D1003	3mm	%	<0.01
Flammability
	UL 94	3mm	-	HB
Processing Condition
Drying Temperature			℃	120
Drying Time			h	5
Injection Temperature			℃	280-300
Mold temperature			℃	80